S 89 Structural stability and ion transport in LaSr2Fe1-yCryO8+δ / V. L. Kozhevnikov, I. A. Leonidov, M. V. Patrakeev, J. A. Bahteeva // NATO Science Series II Mathematics, Physics and Chemistry, 2006, Volume 202, Fuel Cell Technologies State and Perspectives. - 2006. - Vol. 202: Fuel Cell Technologies State and Perspectives. - P149-155 : il. - Bibliogr. : p. 155 (2 ref.) Рубрики: ХИМИЧЕСКИЕ НАУКИ Кл.слова (ненормированные): КИСЛОРОДНАЯ ПРОВОДИМОСТЬ -- ЭЛЕКТРОННАЯ ПРОВОДИМОСТЬ -- ФЕРРИТЫ ЛАНТАН-СТРОНЦИЕВЫЕ -- ПЕРОВСКИТЫ Аннотация: Ceramic samples of LaSr2Fe3-yCryO8+δ are characterized with X-ray powder diffraction and total conductivity measurements in the temperature range 750- 950°C and at oxygen partial pressures between 10-22 and 0.5 atm. It is shown that partial replacement of iron for chromium is an effective means to prevent structural transformation at the loss of oxygen. The isothermal ion conductivity is obtained from the analysis of the total conductivity, and it is shown to decrease with the increase in chromium doping to y = 0.6. However further increase in the chromium content to y = 1 results in an increase in the oxygen ion conductivity level. This behavior is explained with a model where the oxygen ions coordinated to chromium are not excluded entirely from the transport mechanism |